Effect of Cu3P addition on sintering behaviour of elemental powders in the composition of 465 stainless steel
Institute of Powder Metallurgy, Materials Science Department, University of Science and Technology Beijing.ORCID-id: 0000-0003-4888-6237
Institute of Powder Metallurgy, Materials Science Department, University of Science and Technology Beijing.
Institute of Powder Metallurgy, Materials Science Department, University of Science and Technology Beijing.
2006 (Engelska)Ingår i: Powder Metallurgy, ISSN 0032-5899, E-ISSN 1743-2901, Vol. 49, nr 1, s. 28-33Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

The addition of Cu3P for developing the high strength 465 maraging stainless steel from elemental powders was studied. The sintering parameters investigated were sintering temperature, sintering time and wt-%Cu3P. In vacuum sintering, effective sintering took place between 1300 and 1350°C. The maximum sintered density of 7·44 g cm−3 was achieved at 1350°C for 60 min with 4–6 wt-%Cu3P. More than 6 wt-%Cu3P content and temperature >1350°C caused slumping of the specimens. The sintered specimens were heat treated and a maximum ultimate tensile strength (UTS) of 767 MPa was achieved with 4 wt-%Cu3P content. The maximum hardness of 45·5 HRC was achieved in heat treated condition with 4 wt-%Cu3P content. Above 4 wt-%Cu3P content increase in density was observed whereas the response to heat treatment decreased. Fracture morphologies of the sintered specimens were also reported. A comparison of sintering behaviour and mechanical properties of elemental powders with prealloyed powders was also given in the present study

Ort, förlag, år, upplaga, sidor
2006. Vol. 49, nr 1, s. 28-33
Nationell ämneskategori
Annan materialteknik
Forskningsämne
Materialteknik
Identifikatorer
URN: urn:nbn:se:ltu:diva-7224DOI: 10.1179/174329006X89344Lokalt ID: 58e3b694-1f98-445f-a9cd-1e89ad0e79a0OAI: oai:DiVA.org:ltu-7224DiVA, id: diva2:980113
Anmärkning
Upprättat; 2006; 20150416 (farakh)Tillgänglig från: 2016-09-29 Skapad: 2016-09-29 Senast uppdaterad: 2017-11-24Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltext

Personposter BETA

Akhtar, Farid

Sök vidare i DiVA

Av författaren/redaktören
Akhtar, Farid
I samma tidskrift
Powder Metallurgy
Annan materialteknik

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 125 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf