Effect of additive Cu-10Sn alloy on sintering Behavior of elemental powders in composition of 465 stainless steel
Department of Metallurgical and Materials Engineering, University of Engineering and Technology, Lahore.ORCID-id: 0000-0003-4888-6237
2007 (Engelska)Ingår i: Journal of Iron and Steel Research International, ISSN 1006-706X, E-ISSN 2210-3988, Vol. 14, nr 4, s. 61-74Artikel i tidskrift (Refereegranskat) Published
Abstract [en]

The addition of Cu-10Sn alloy for developing the high strength 465 maraging stainless steel from elemental powders was studied. The sintering parameters investigated include the sintering temperature, the sintering time, and the mass percent of Cu-10Sn. For vacuum sintering, effective sintering occurs at temperature between 1250°C and 1300°C. The maximum sintered density was achieved at 1300°C for 60 min with 3% (in mass percent) Cu-10Sn alloy. More than 3% (in mass percent) Cu-10Sn content and temperature above 1300°C caused slumping of the samples. A maximum density of 7.4 g/cm3 was achieved with 3% (in mass percent) Cu-10Sn content at a sintering temperature of 1300°C for 60 min. A maximum ultimate tensile strength (UTS) of 517 MPa was achieved with 3% (in mass percent) Cu-10Sn content. With content higher than 2% (in mass percent) Cu-10Sn, a maximum increase in the density was observed. The fracture morphologies of the sintered samples are also reported.

Ort, förlag, år, upplaga, sidor
2007. Vol. 14, nr 4, s. 61-74
Nationell ämneskategori
Annan materialteknik
Forskningsämne
Materialteknik
Identifikatorer
URN: urn:nbn:se:ltu:diva-12935DOI: 10.1016/S1006-706X(07)60059-4Lokalt ID: c14fefcc-3d25-43c4-93fe-1fc1284ccf5eOAI: oai:DiVA.org:ltu-12935DiVA, id: diva2:985886
Anmärkning
Upprättat; 2007; 20150416 (farakh)Tillgänglig från: 2016-09-29 Skapad: 2016-09-29 Senast uppdaterad: 2017-11-24Bibliografiskt granskad

Open Access i DiVA

Fulltext saknas i DiVA

Övriga länkar

Förlagets fulltext

Personposter BETA

Akhtar, Farid

Sök vidare i DiVA

Av författaren/redaktören
Akhtar, Farid
I samma tidskrift
Journal of Iron and Steel Research International
Annan materialteknik

Sök vidare utanför DiVA

GoogleGoogle Scholar

doi
urn-nbn

Altmetricpoäng

doi
urn-nbn
Totalt: 422 träffar
RefereraExporteraLänk till posten
Permanent länk

Direktlänk
Referera
Referensformat
  • apa
  • harvard1
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annat format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annat språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf