Influence of cryogenic cyclic aging on thermal, mechanical and tribological performance of PI-based materials
Luleå University of Technology, Department of Engineering Sciences and Mathematics, Machine Elements. CEMMPRE, Department of Mechanical Engineering, University of Coimbra, Portugal.ORCID iD: 0000-0002-8025-5104
CEMMPRE, Department of Mechanical Engineering, University of Coimbra, Portugal.
Luleå University of Technology, Department of Engineering Sciences and Mathematics, Machine Elements.ORCID iD: 0000-0001-8676-8819
(English)Manuscript (preprint) (Other academic)
Keywords [en]
PI composite, tribology, cryogenic cyclic aging, vacuum
National Category
Tribology (Interacting Surfaces including Friction, Lubrication and Wear)
Identifiers
URN: urn:nbn:se:ltu:diva-105595OAI: oai:DiVA.org:ltu-105595DiVA, id: diva2:1860629
Available from: 2024-05-24 Created: 2024-05-24 Last updated: 2024-05-27
In thesis
1. Tribological and Mechanical Performance of Thermoplastic Composites: Effect of Cryogenic Aging and Testing-Environment
Open this publication in new window or tab >>Tribological and Mechanical Performance of Thermoplastic Composites: Effect of Cryogenic Aging and Testing-Environment
2024 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

Recent advancements in energy, space, medicine, and transportation sectors have raised the demand for high-performing materials capable of functioning under demanding conditions such as low temperatures, vacuum, and cryogenic liquids like liquid nitrogen, natural gas, and hydrogen. Besides exposure to cryogenic environments, materials must withstand extensive loads and temperature gradients, inevitably leading to decreases in material properties, premature wear, reduced service life, and early failure due to aging. The performance of various components, including valves, bearings, seals, and gaskets, often determines the overall system performance.

High-performance thermoplastic polymers, particularly polyetheretherketone (PEEK) and polyimide (PI), are favourable candidates for demanding tribological applications due to their exceptional mechanical, chemical, and thermal properties. Although PEEK and PI-based materials have been utilised for cryogenic applications, they still do not fully meet all the requirements. To improve their mechanical properties and tribological performance, various modifications and fillers, including carbon fibres and solid lubricants such as graphite, molybdenum disulphide (MoS2), and polytetrafluoroethylene (PTFE), are introduced. While most studies focus on their behaviour in ambient conditions, ambiguities remain regarding their performance and failure mechanisms in demanding environments. Moreover, there has been limited investigation on the impact of long-term or cyclic exposure to cryogenic temperatures and liquids on the properties of polymers and polymer composites. 

This thesis investigates thermal, thermo-mechanical, and mechanical properties, as well as the tribological performance, of selected commercially available high-performance thermoplastic composites based on PEEK and PI matrices under varying test conditions. Friction behaviour and wear mechanisms of the materials were studied in detail in air and vacuum at 25 °C, as well as in vacuum at –100 °C. Thermo-mechanical and mechanical properties, as well as failure mechanisms, were examined in a temperature range from –195 °C to 25 °C. Furthermore, the thermal, mechanical, and tribological performance of PEEK and PIbased materials were further evaluated at 25 °C after the materials underwent two types of cryogenic aging: 1) long-term cryogenic aging in liquid nitrogen at –196 °C for 5 months, and 2) cyclic-aging for 12 weeks; each cycle was 7 days and included two steps: 6 days in liquid nitrogen at –196 °C and 1 day in an oven at 40 °C.

The results show that material performance and wear mechanisms are significantly influenced by the test environment, temperature, and cryogenic aging, depending on polymer structure and composition. Variations in polymer structure and the addition of fillers improved mechanical properties at room and low temperatures without significantly affecting thermal properties. Polymer matrix physical shrinkage at low temperatures enhanced the filler/matrix interface, resulting in fracture toughness improvements of up to 40% for PEEK and 150% for PI. However, thermal stresses at the interface with carbon fibres and graphite competed with matrix toughening.

In vacuum environment, PEEK exhibited a lower coefficient of friction, but a higher wear rate compared to its performance in air, mainly due to desorption of water molecules. The tribological performance of PEEK improved with the addition of carbon fibres, graphite, and PTFE. PI1 maintained consistent performance across all environments, while PI5 displayed notable variations, including a very low coefficient of friction in vacuum. The addition of MoS2 or graphite to PI1 reduced the coefficient of friction and wear rate enhancing transfer film formation, and PTFE mitigated significant changes.

At low temperature in vacuum, improved toughness allowed PEEK to withstand increased contact pressure, reducing the wear rate. PEEK composites with carbon fibres, graphite, and PTFE showed a very low coefficient of friction (0.02). In contrast, PI experienced increased coefficient of friction and wear rate due to high contact stresses and abrasive wear. The formation of a thin, homogeneous transfer film on the countersurface and polymer disk was advantageous in reducing friction and wear.

Cryogenic aging caused embrittlement in PEEK-based materials and neat PI due to incomplete chain relaxation, but it improved the filler/matrix interface in PI composites, enhancing fracture toughness by 58% for the PI/MoS2 composite. While neat polymers experienced minimal effects, some composites showed up to a 220% increase in wear rate. Cryogenic cyclic aging demonstrated that PEEK was more sensitive to aging than PI, with a 22% reduction in fracture toughness for PEEK and up to a 93% increase for PI. Tribological tests indicated increased abrasive wear for unreinforced polymers and pronounced adhesive wear for composites, leading to more homogeneous transfer film generation. In vacuum, the wear rate of aged graphite-reinforced PI increased dramatically by 10920%.

The outcome of the presented research demonstrates the need for custom-designed polymer-based materials to fit specific demanding tribological applications, and consider cryogenic aging effect on polymer properties, which is not currently the case.

Place, publisher, year, edition, pages
Luleå: Luleå University of Technology, 2024
Series
Doctoral thesis / Luleå University of Technology 1 jan 1997 → …, ISSN 1402-1544
National Category
Tribology (Interacting Surfaces including Friction, Lubrication and Wear)
Research subject
Machine Elements
Identifiers
urn:nbn:se:ltu:diva-105597 (URN)978-91-8048-589-0 (ISBN)978-91-8048-590-6 (ISBN)
Public defence
2024-09-03, E632, Luleå University of Technology, Luleå, 09:00 (English)
Opponent
Supervisors
Available from: 2024-05-27 Created: 2024-05-27 Last updated: 2024-08-01Bibliographically approved

Open Access in DiVA

No full text in DiVA

Authority records

Nikonovich, MaksimEmami, Nazanin

Search in DiVA

By author/editor
Nikonovich, MaksimEmami, Nazanin
By organisation
Machine Elements
Tribology (Interacting Surfaces including Friction, Lubrication and Wear)

Search outside of DiVA

GoogleGoogle Scholar

urn-nbn

Altmetric score

urn-nbn
Total: 58 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf