The addition of Cu3P for developing the high strength 465 maraging stainless steel from elemental powders was studied. The sintering parameters investigated were sintering temperature, sintering time and wt-%Cu3P. In vacuum sintering, effective sintering took place between 1300 and 1350°C. The maximum sintered density of 7·44 g cm−3 was achieved at 1350°C for 60 min with 4–6 wt-%Cu3P. More than 6 wt-%Cu3P content and temperature >1350°C caused slumping of the specimens. The sintered specimens were heat treated and a maximum ultimate tensile strength (UTS) of 767 MPa was achieved with 4 wt-%Cu3P content. The maximum hardness of 45·5 HRC was achieved in heat treated condition with 4 wt-%Cu3P content. Above 4 wt-%Cu3P content increase in density was observed whereas the response to heat treatment decreased. Fracture morphologies of the sintered specimens were also reported. A comparison of sintering behaviour and mechanical properties of elemental powders with prealloyed powders was also given in the present study