This article discusses the fracture modelling accuracy of strain-driven ductile fracture models when introducing damage of high strength sheet steel. Numerical modelling of well-known fracture mechanical tests was conducted using a failure and damage model to control damage and fracture evolution. A thorough validation of the simulation results was conducted against results from laboratory testing. Such validations show that the damage and failure model is suited for modelling of material failure and fracture evolution of specimens without damage. However, pre-damaged specimens show less correlation as the damage and failure model over-predicts the displacement at crack initiation with an average of 28%. Consequently, the results in this article show the need for an extension of the damage and failure model that accounts for the fracture mechanisms at the crack tip. Such extension would aid in the improvement of fracture mechanical testing procedures and the modelling of high strength sheet metal manufacturing, as several sheet manufacturing processes are defined by material fracture.

Shear cutting introduces residual strains, notches and cracks, which negatively affects edge-formability. This is especially relevant for forming of high-strength sheets, where edge-cracking is a serious industrial problem. Numerical modelling of the shear cutting process can aid the understanding of the sheared edge damage and help preventing edge-cracking. However, modelling of the shear cutting process requires robust and accurate numerical tools that handle plasticity, large deformation and ductile failure. The use of conventional finite element methods (FEM) may give rise to distorted elements or loss of accuracy during re-meshing schemes, while mesh-free methods have tendencies of tensile instability or excessive computational cost. In this article, the authors propose the particle finite element method (PFEM) for modelling the shear cutting process of high-strength steel sheets, acquiring high accuracy results and overcoming the stated challenges associated with FEM. The article describe the implementation of a mixed axisymmetric formulation, with the novelty of adding a ductile damage- and failure model to account for material fracture in the shear-cutting process. The PFEM shear-cutting model was validated against experiments using varying process parameters to ensure the predictive capacity of the model. Likewise, a thorough sensitivity analysis of the numerical implementation was conducted. The results show that the PFEM model is able to predict the process forces and cut edge shapes over a wide range of cutting clearances, while efficiently handling the numerical challenges involved with large material deformation. It is thus concluded that the PFEM implementation is an accurate predictive tool for sheared edge damage assessment.

The study examines the shear cutting process of Advanced High Strength Steel using the Particle Finite Element Method. Shear cutting, a crucial process in sheet metal forming, often leads to microcracks and plastic deformation that degrades the material performance in subsequent applications, such as cold forming, crashworthiness, and fatigue resistance. This work utilises the Particle Finite Element Method as an alternative to conventional Finite Element Methods to address the challenges of large deformation solid mechanics, offering high predictive accuracy in localised shearing deformation and fracture. The model was validated against experimental data from sheet punching tests, with evaluations at both macroscopic and mesoscopic levels, including cut edge profiles and microstructural deformation within the shear-affected zone. The Particle Finite Element Method approach demonstrated a high level of accuracy in predicting cut edge shape and shear-induced damage across various cutting conditions. As an unconventional numerical technique, usage of the Particle Finite Element Method advances modelling of large deformations solid mechanics and providing a robust tool for optimising manufacturing processes of materials sensitive to sheared edge damage.